Quality values.
HIPS
| Units | Test methods | UPM 905 | UPM 808 | UPM 705 | UPM 1705 | UPM 1004f | UPM 607 | UPM 1104TG | UPM 1905 |
|---|---|---|---|---|---|---|---|---|---|
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 |
| Melt flow index (200°Ñ, 5 kg) | |||||||||
| g/10 min | GOST 11645-73 ASTM D-1238 | 2,5 ± 4,5 | 4 ± 6 | 6 ± 8 | 3 ± 5 | 2 ± 4 | 6 ± 8 | 3 ± 5 | 3 ± 5 |
| Izod impact strength (3,2 mm) | |||||||||
| kJ/m2 J/m |
GOST 19109-84 ASTM D-256(A) ISO 180 |
11 112 | 8 81 | 7 71 | 14 142 |
8 81 | 10 102 | 9 91 | 8 81 |
| Tensile strength (5 mm/min) | |||||||||
| MPa | GOST 11262-80 ASTM D-638 | 21 | 22 | 24 | 19 | 22 | 23 | 19 | 22 |
| Relative elongation at break (5 mm/min) | |||||||||
| % | GOST 11262-80 ASTM D-638 | 45 | 40 | 30 | 50 | 50 | 30 | 25 | 60 |
| Vicat softening point (5 kg, 50°C/hr) | |||||||||
| °Ñ | GOST 15088-83 ASTM D-1525 | 90 | 90 | 88 | 90 | 90 | 90 | 88 | 91 |
| Residual monomer content | |||||||||
| % | GOST 15820-82 | 0,05 | 0,05 | 0,05 | 0,05 | 0,05 | 0,05 | 0,05 | 0,05 |
| MFI range of one lot | |||||||||
| % | Plastpolymer method | ±10 | ±10 | ±10 | ±10 | ±10 | ±10 | ±10 | ±10 |
| Gloss (60° angle) | |||||||||
| % | Plastpolymer method | — | — | — | — | — | 70 | — | — |
| Stability to Freon 141 and 11 and cyclopentene | |||||||||
| % | ISO 4599-1986E Plastpolymer method | — | — | — | — | 70 | — | — | — |
| Inflammability | |||||||||
| UL-94 | HB | HB | HB | HB | HB | HB | V-O | HB | |